1. – Department Of Science & Humanities, M. Kumarasamy College Of Engineering, Karur, Tamil Nadu, India.
| Received
05-Aug-2019 |
Accepted
- |
Published
05-Aug-2019 |
Abstract
P-CaP (p-chloroanilinepthalic acid) single crystal was grown by slow evaporation technique. A single Crystal XRD study reveals that the grown crystal belongs to orthorhombic system. Decomposition mechanism and melting point of the sample were deliberated in TGA/DSC analysis. Transmission ability of the crystal in the visible was tested by recording UV-VIS-NIR spectrum also Mechanical strength of the material is determined by Vickers hardness test. The FTIR Spectrum was recorded in the range of 400 cm-1 and 4000 cm-1 which is confirmed the formation of p-CaP crystal.